Lightweight strength designed for dynamic, high-load applications
ROHACELL® 200 HERO
At 205 kg/m³, ROHACELL® 200 HERO is the densest of the 4 grades in the ROHACELL® HERO range.
Innovative ROHACELL® HERO delivers the latest in materials technology for composite aircraft structures that are lightweight, durable over their lifetime and less expensive to produce. It’s the new standard in aircraft structural core material.
Mechanical properties
- Density
- 205 kg/m³
- 12.80 lbs/ft³
- Compressive Strength
- 7.1 MPa
- 1,030 psi
- Tensile Strength
- 12.3 MPa
- 1,784 psi
- Shear Strength
- 5.2 MPa
- 754 psi
- Elastic Modulus
- —
- Shear Modulus
- 109 MPa
- 15,809 psi
- Strain at Break
- 10.8 %
Compare ROHACELL® HERO grades
Properties
Density
52kg/m³
3.25lbs/ft³
75kg/m³
4.68lbs/ft³
110kg/m³
6.87lbs/ft³
205kg/m³
12.80lbs/ft³
Compressive Strength
0.6MPa
87psi
1.1MPa
160psi
2.5MPa
363psi
7.1MPa
1,030psi
Tensile Strength
2.6MPa
377psi
4.1MPa
595psi
6.3MPa
914psi
12.3MPa
1,784psi
Shear Strength
0.7MPa
102psi
1.3MPa
189psi
2.3MPa
334psi
5.2MPa
754psi
Elastic Modulus
—
—
—
—
—
—
—
—
Shear Modulus
22MPa
3,191psi
28MPa
4,061psi
50MPa
7,252psi
109MPa
15,809psi
Strain at Break
8%
9.5%
9.9%
10.8%