Industrial-grade performance for versatile, reliable results
ROHACELL® 110 IGF
At 110 kg/m³, ROHACELL® 110 IGF is the densest of the 4 grades in the ROHACELL® IG/IG-F range.
ROHACELL® IG-F structural foam is a closed-cell rigid foam based on polymethacrylimide (PMI) chemistry and contains no CFC's. The “IG” in ROHACELL® IG-F stands for “Industrial grade.” It is the standard product in our range of rigid foam products and is suitable for a wide variety of automotive, medical and industrial applications. The “F” in ROHACELL® IG-F indicates the foam’s fine cell structure that will take up only minimal resin at the surface where the cells have been cut open. Less resin take-up during part processing means less final part weight and overall cost.
Mechanical properties
- Density
- 110 kg/m³
- 6.87 lbs/ft³
- Compressive Strength
- 3 MPa
- 435 psi
- Tensile Strength
- 3.5 MPa
- 508 psi
- Shear Strength
- 2.4 MPa
- 348 psi
- Elastic Modulus
- —
- Shear Modulus
- 50 MPa
- 7,252 psi
- Strain at Break
- —
Compare ROHACELL® IG/IG-F grades
Grades
Properties
Density
32kg/m³
2.00lbs/ft³
52kg/m³
3.25lbs/ft³
75kg/m³
4.68lbs/ft³
110kg/m³
6.87lbs/ft³
Compressive Strength
0.4MPa
58psi
0.9MPa
131psi
1.5MPa
218psi
3MPa
435psi
Tensile Strength
1MPa
145psi
1.9MPa
276psi
2.8MPa
406psi
3.5MPa
508psi
Shear Strength
0.4MPa
58psi
0.8MPa
116psi
1.3MPa
189psi
2.4MPa
348psi
Elastic Modulus
36MPa
5,221psi
70MPa
10,153psi
92MPa
13,343psi
—
—
Shear Modulus
13MPa
1,885psi
19MPa
2,756psi
29MPa
4,206psi
50MPa
7,252psi
Strain at Break
—
—
—
—