ROHACELL® 110 WF
At 110 kg/m³, ROHACELL® 110 WF sits between 71 WF and 200 WF in the ROHACELL® WF-HT range.
ROHACELL® WF foam core has been specifically designed for the use in the aerospace industry. Based on polymethacrylimide (PMI) chemistry, it is engineered to meet demanding requirements from aircraft manufacturers and has led to many specifications for more than 30 years, including MIL-PRF-46194A, WL 5.1460, WL 5.1461 and others.
Mechanical properties
- Density
- 110 kg/m³
- 6.87 lbs/ft³
- Compressive Strength
- 3.6 MPa
- 522 psi
- Tensile Strength
- 3.7 MPa
- 537 psi
- Shear Strength
- 2.4 MPa
- 348 psi
- Elastic Modulus
- 180 MPa
- 26,107 psi
- Shear Modulus
- 70 MPa
- 10,153 psi
- Strain at Break
- 3 %
Compare ROHACELL® WF-HT grades
Properties
Density
52kg/m³
3.25lbs/ft³
75kg/m³
4.68lbs/ft³
110kg/m³
6.87lbs/ft³
205kg/m³
12.80lbs/ft³
Compressive Strength
0.8MPa
116psi
1.7MPa
247psi
3.6MPa
522psi
9MPa
1,305psi
Tensile Strength
1.6MPa
232psi
2.2MPa
319psi
3.7MPa
537psi
6.8MPa
986psi
Shear Strength
0.8MPa
116psi
1.3MPa
189psi
2.4MPa
348psi
5MPa
725psi
Elastic Modulus
75MPa
10,878psi
105MPa
15,229psi
180MPa
26,107psi
350MPa
50,763psi
Shear Modulus
24MPa
3,481psi
42MPa
6,092psi
70MPa
10,153psi
150MPa
21,756psi
Strain at Break
3%
3%
3%
3.5%